Reaction-bonding of ALUMINUM OXIDE (cas 11092-32-3) processed by binder jetting
-
Add time:07/16/2019 Source:sciencedirect.com
The combination of additive manufacturing based on the binder jetting and reaction-bonding ALUMINUM OXIDE (cas 11092-32-3) (RBAO) techniques can produce fully ceramic specimens near net shape. This study developed powder formulations composed of stearic acid coated aluminum (Al) powder and dextrin coated aluminum oxide (Al2O3) powder, in order to be processed via binder jetting, and post-processed via RBAO. The coated powders were mixed with different volume ratios of Al to Al2O3. After the printing process, the specimens were heat treated from room temperature to 1200 °C, in an oxidative atmosphere. Increasing Al volume ratio from 0.25 to 0.50 generated a significant flexural strength improvement, reaching about 20%. This increase had no influence on apparent porosity or density, which averaged at 64% and 1.35 g cm−3, respectively. A complex geometry model was built to prove the feasibility of producing sophisticated parts. As expected, post-RBAO parts shrinkage was nearly zero, proving the feasibility of the additive manufacturing, by binder jetting, and RBAO combination.
We also recommend Trading Suppliers and Manufacturers of ALUMINUM OXIDE (cas 11092-32-3). Pls Click Website Link as below: cas 11092-32-3 suppliers
Prev:Antiproliferative, cytotoxic and apoptotic activity of the bentonite transformation of sesquiterpene lactone glaucolide B (cas 11091-27-3) to 5β-hydroxy-hirsutinolide on tumor cell lines
Next:Low-temperature laser generated ultrathin ALUMINUM OXIDE (cas 11092-32-3) layers for effective c-Si surface passivation) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Influence of plasmon resonance in silver nanoparticles on the properties of stimulated emission of 1,3,5,7,8-pentamethyl-2,6-diethylpyrromethene-difluoroborate molecules in film of porous ALUMINUM OXIDE (cas 11092-32-3)07/25/2019
- Interaction of poly(acrylic acid) and ALUMINUM OXIDE (cas 11092-32-3) particles in suspension: Particle size effect07/24/2019
- Durable omniphobicity of oil-impregnated anodic ALUMINUM OXIDE (cas 11092-32-3) nanostructured surfaces07/23/2019
- Effect of milling on the oxidation kinetics of Aluminium + Boron mixture and nanocrystalline Aluminium Boride (AlB12)07/22/2019
- Interaction of Poly(dimethylsiloxane) and octamethylcyclotetrasiloxane with ALUMINUM OXIDE (cas 11092-32-3)s comprising different acid-base properties07/20/2019
- Hepato-renal toxicity of oral sub-chronic exposure to ALUMINUM OXIDE (cas 11092-32-3) and/or zinc oxide nanoparticles in rats07/21/2019
- Synergistic effect of poly(3,4-ethylenedioxythiophene), reduced graphene oxide and aluminium oxide) as counter electrode in dye-sensitized solar cell07/19/2019
- Oxidation protection of aluminum metaphosphate coating prepared by cathodic electrochemical treatment for graphite07/18/2019
- Low-temperature laser generated ultrathin ALUMINUM OXIDE (cas 11092-32-3) layers for effective c-Si surface passivation07/17/2019
-
Health and Chemical more >
-
Related Products
- Aluminum 1,4,8,11,15,18,22,25-octabutoxy-29H,31H-phthalocyanine triethylsiloxide
- Aluminum aceglutamide
- Aluminum Acetate
- Aluminum acetylacetonate
- Aluminum ammonium sulfate
- Aluminum arsenide(AlAs)
- ALUMINUM AZIDE
- Aluminum barium magnesium oxide
- Aluminum barium titanium oxide
- Aluminum bismuth oxide(Al3BiO6), monohydrate (9CI)