Functionalized polysulfide copolymers with 4-Vinylpyridine (cas 100-43-6) via inverse vulcanization
-
Add time:07/19/2019 Source:sciencedirect.com
A new series of functional polysulfide copolymers called poly(sulfur-random-4-Vinylpyridine (cas 100-43-6)) (poly(S-r-4VP)) was synthesized via inverse vulcanization technique by ring opening polymerization of elemental sulfur in the presence of 4-vinylpyridine (4VP). The corresponding copolymers can be post functionalized by using amine group in 4VP unit to get polymers bearing various properties. Elemental sulfur was heated up to 160 °C and 4VP was added slowly to a clear yellowish orange colored liquid at this temperature. The reaction mixture was vitrified to form a reddish-brown polymeric material at 180 °C in 1 h. The products were characterized by using FTIR, NMR, and Raman spectroscopic techniques. Poly(S-r-4VP) copolymers are soluble in common solvents like dichloromethane, chloroform and tetrahydrofuran. Weight-average molecular weights of poly(S-r-4VP) copolymers with different wt% 4VP were measured by using gel permeation chromatography technique. The polysulfide copolymers with different wt% 4VP have high weight-average molecular weights with polydispersity indeces (PDI) in a range from 1.88 to 4.06 measured by gel permeation chromatography. Post functionalization of the copolymer with 50 wt% 4VP as an example was performed successfully by using alkyl bromide to get N-alkyl quaternized 4VP in polymer backbone.
We also recommend Trading Suppliers and Manufacturers of 4-Vinylpyridine (cas 100-43-6). Pls Click Website Link as below: cas 100-43-6 suppliers
Prev:Vasorelaxant effects of 1-nitro-2-Phenylethene (cas 100-42-5) in rat isolated aortic rings
Next:4-Vinylpyridine (cas 100-43-6)-modified post-cross-linked resins and their adsorption of phenol and Rhodamine B) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Radiation induced emulsion graft polymerization of 4-Vinylpyridine (cas 100-43-6) onto PE/PP nonwoven fabric for As(V) adsorption07/28/2019
- pH-Sensitive electrical behavior of 4-Vinylpyridine (cas 100-43-6) grafts on poly(propylene) films07/27/2019
- Gold nanoparticles stabilized by poly(4-Vinylpyridine (cas 100-43-6)) grafted cellulose nanocrystals as efficient and recyclable catalysts07/26/2019
- A simple and green methodology to assemble poly(4-Vinylpyridine (cas 100-43-6)) and a sulfonated azo-dye for obtaining stable polymeric nanoparticles07/25/2019
- Poly(4-Vinylpyridine (cas 100-43-6)) polyHIPEs as catalysts for cycloaddition click reaction07/24/2019
- Analysis of the formation process and performance of magnetic Fe3O4@Poly(4-Vinylpyridine (cas 100-43-6)) absorbent prepared by in-situ synthesis07/23/2019
- Selective introduction of a trifluoroacetyl group onto 4-Vinylpyridine (cas 100-43-6)s through magnesium-promoted reduction07/22/2019
- Poly(4-Vinylpyridine (cas 100-43-6)) based novel stationary phase investigated under supercritical fluid chromatography conditions07/20/2019
- 4-Vinylpyridine (cas 100-43-6)-modified post-cross-linked resins and their adsorption of phenol and Rhodamine B07/21/2019