pH-Sensitive electrical behavior of 4-Vinylpyridine (cas 100-43-6) grafts on poly(propylene) films
-
Add time:07/27/2019 Source:sciencedirect.com
An interesting, electrical behavior of Poly(4-Vinylpyridine (cas 100-43-6)) was observed at different pH values. 4-vinylpyridine was grafted onto mechanically durable poly(propylene) films to synthesize a pH responsive hydrogel. We have focused on the influence of temperature and pH on the electrical behavior response of hydrogel. An abrupt increase of its electrical resistance from 5 to 20 X106 Ω was observed when the hydrogel (100% grafted) was swelled on phosphate buffer solutions with pH value of 4 and 8 respectively.
We also recommend Trading Suppliers and Manufacturers of 4-Vinylpyridine (cas 100-43-6). Pls Click Website Link as below: cas 100-43-6 suppliers
Prev:Gold nanoparticles stabilized by poly(4-Vinylpyridine (cas 100-43-6)) grafted cellulose nanocrystals as efficient and recyclable catalysts
Next:Radiation induced emulsion graft polymerization of 4-Vinylpyridine (cas 100-43-6) onto PE/PP nonwoven fabric for As(V) adsorption) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Radiation induced emulsion graft polymerization of 4-Vinylpyridine (cas 100-43-6) onto PE/PP nonwoven fabric for As(V) adsorption07/28/2019
- Gold nanoparticles stabilized by poly(4-Vinylpyridine (cas 100-43-6)) grafted cellulose nanocrystals as efficient and recyclable catalysts07/26/2019
- A simple and green methodology to assemble poly(4-Vinylpyridine (cas 100-43-6)) and a sulfonated azo-dye for obtaining stable polymeric nanoparticles07/25/2019
- Poly(4-Vinylpyridine (cas 100-43-6)) polyHIPEs as catalysts for cycloaddition click reaction07/24/2019
- Analysis of the formation process and performance of magnetic Fe3O4@Poly(4-Vinylpyridine (cas 100-43-6)) absorbent prepared by in-situ synthesis07/23/2019
- Selective introduction of a trifluoroacetyl group onto 4-Vinylpyridine (cas 100-43-6)s through magnesium-promoted reduction07/22/2019
- Poly(4-Vinylpyridine (cas 100-43-6)) based novel stationary phase investigated under supercritical fluid chromatography conditions07/20/2019
- 4-Vinylpyridine (cas 100-43-6)-modified post-cross-linked resins and their adsorption of phenol and Rhodamine B07/21/2019
- Functionalized polysulfide copolymers with 4-Vinylpyridine (cas 100-43-6) via inverse vulcanization07/19/2019