Gold nanoparticles stabilized by poly(4-Vinylpyridine (cas 100-43-6)) grafted cellulose nanocrystals as efficient and recyclable catalysts
-
Add time:07/26/2019 Source:sciencedirect.com
pH-responsive poly(4-vinylpyridine) (P4VP) grafted cellulose nanocrystals (P4VP-g-CNC) were prepared by Surface-Initiated Atom Transfer Radical Polymerization (SI-ATRP) and subsequently used to stabilize gold nanoparticles (Au NPs) as efficient and recyclable nanocatalysts for the reduction of 4-nitrophenol (4NP). The presence of P4VP brushes on the CNC surface controlled the growth of Au NPs yielding smaller averaged diameter compared to Au NPs deposited directly on pristine CNC. The catalytic performances of pristine Au NPs, [email protected] and [email protected]-g-CNC were compared by measuring the turnover frequency (TOF) for the catalytic reduction of 4NP. Compared to pristine Au NPs, the catalytic activity of [email protected] and [email protected]-g-CNC were 10 and 24 times better. Moreover, the [email protected]-g-CNC material could be recovered via flocculation at pH > 5, and the recycled nanocatalyst remained highly active.
We also recommend Trading Suppliers and Manufacturers of 4-Vinylpyridine (cas 100-43-6). Pls Click Website Link as below: cas 100-43-6 suppliers
Prev:A simple and green methodology to assemble poly(4-Vinylpyridine (cas 100-43-6)) and a sulfonated azo-dye for obtaining stable polymeric nanoparticles
Next:pH-Sensitive electrical behavior of 4-Vinylpyridine (cas 100-43-6) grafts on poly(propylene) films) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Radiation induced emulsion graft polymerization of 4-Vinylpyridine (cas 100-43-6) onto PE/PP nonwoven fabric for As(V) adsorption07/28/2019
- pH-Sensitive electrical behavior of 4-Vinylpyridine (cas 100-43-6) grafts on poly(propylene) films07/27/2019
- A simple and green methodology to assemble poly(4-Vinylpyridine (cas 100-43-6)) and a sulfonated azo-dye for obtaining stable polymeric nanoparticles07/25/2019
- Poly(4-Vinylpyridine (cas 100-43-6)) polyHIPEs as catalysts for cycloaddition click reaction07/24/2019
- Analysis of the formation process and performance of magnetic Fe3O4@Poly(4-Vinylpyridine (cas 100-43-6)) absorbent prepared by in-situ synthesis07/23/2019
- Selective introduction of a trifluoroacetyl group onto 4-Vinylpyridine (cas 100-43-6)s through magnesium-promoted reduction07/22/2019
- Poly(4-Vinylpyridine (cas 100-43-6)) based novel stationary phase investigated under supercritical fluid chromatography conditions07/20/2019
- 4-Vinylpyridine (cas 100-43-6)-modified post-cross-linked resins and their adsorption of phenol and Rhodamine B07/21/2019
- Functionalized polysulfide copolymers with 4-Vinylpyridine (cas 100-43-6) via inverse vulcanization07/19/2019